HBW480Cr2 Wear Plate

  • Brand: EB
  • Product type:Wear Plate
  • Heat-resistant Steel Plate
  • High-temperature Alloy Plate
  • Hardox Plates
  • Bisplate
  • NM Plate
  • High Mn Steel Plate






    Categories: , Tag:

    Description

    ZAlCu10 High precision Alu Cast Parts EB9090

    Wear Plate

    • Wear Plate for Shot Blast Machines, Chutes, Clinker Silo,Port Machinery and Ball Mills is as below:
    • Wear Plate of this specification covers a group of white cast irons that have been alloyed to secure high resistance to
    • abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.
    • These alloys are made by melting process and shall have microstructures that consist of carbides, martensite,
    • bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite. The following conditions for
    • casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened
    • for machining. Heat treatment shall be done. The chemical composition of a class and type (that is, Class I, Type A)
    • shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum,
    • copper, phosphorus, and sulfur. Hardness test shall also be made.
    • Wear Plate Thickness :10mm, 12mm, 14mm, 15mm, 16mm, 18mm, 20mm, 15mm, 30mm, 32mm, 40mm,
    • 50mm, 60mm, 80mm, 100mm, 200mm, 500mm, 1000mm.
    • Section Thickness for Wear Plate:1 inch, 2″, 3″, 4″, 5″, 8″, 10″, 20″, 30″, 40″.
    • Material Grade: Cr-Mo Alloy Steel(ZG50Cr5Mo,ZG60Cr6Mo,Cr12Mo), high Cr white iron(BTMCr15Mo,BTMCr20Mo,BTMCr26Mo)

    Our Capability for Wear Plate is as below:

    We can fabricate the wear plate as per your material and your sizes.

    We’d like to help select suitable material grade for your wear plates as per your specific working condition.

    Material Grades & Alloys for Wear Plates & Chute Liners are as below:

    1. High Cr White Iron Cast Wear Plate

    ISO 21988/JN/ HBW C Si Mn P s Cr Ni Mo Cu
    HBW555XCr13 555 1.8-3.6 1.0 0.5-1.5 0.08 0.08 11-14 2.0 3.0 1.2
    HBW555XCr16 555 1.8-3.6 1.0 0.5-1.5 0.08 0.08 14-18 2.0 3.0 1.2
    HBW555XCr21 555 1.8-3.6 1.0 0.5-1.5 0.08 0.08 18-23 2.0 3.0 1.2
    HBW555XCr27 555 1.8-3.6 1.0 0.5-1.5 0.08 0.08 23-30 2.0 3.0 1.2
    HBW600XCr35 600 3.0-5.5 1.0 1.0-3.0 0.06 0.06 30-40 1.0 1.5 1.2
    HBW600XCr20Mo2Cu 600 3.0-5.5 1.0 1.0 0.06 0.06 18-21 1.0 1.4-2.0 0.8-1.2

    2. Nihard White Iron Cast Wear Plate

    Handelsname Kurzzeichen W.St.Nr.

    Hardness for Ni-hard 1 is  ≥ HB500   G-X 330 NiCr 4 2 0.9625

    Hardness for Ni-hard 2 is ≥ HB550   G-X 3260 NiCr 4 2 0.9620

    Hardness for Ni-hard 4 is ≥ HB600,  HB630 G-X 300 NiCrSi 9 5 2 0.9630

    G-X 300 NiMo 15 3 0.9635

    G-X 260 Cr 27 0.9635

    ISO 21988/JN/ HBW C Si Mn P S Ni Cr
    HBW480Cr2 480 2.5-3.0 0.8 0.8 0.10 0.10 3.0-5.5 1.5-3.0
    HBW500Cr9 500 2.4-2.8 1.5-2.2 0.2-0.8 0.06 0.06 4.0-5.5 8.0-10.0
    HBW510Cr2 510 30.-3.6 0.8 0.8 0.10 0.10 3.0-5.5 1.5-3.0
    HBW555Cr9 555 2.5-3.5 1.5-2.5 0.3-0.8 0.08 0.08 4.5-6.5 8.0-10.0
    HBW630Cr9 630 3.2-3.6 1.5-2.2 0.2-0.8 0.06 0.06 4.0-5.5 8.0-10.0

    3. Hardness for Martensitic Cr- Mo Alloy Steel Plate is ≥HRC48

    4. The hardness of Pearlitic Cr-Mo Alloy Steel Plates is HB310-375

    5. Heat-resistant Steel Plates.

    6. High-temperature Alloy Plates.

    7. Hardox Plates:

    HARDOX400,HARDOX450, HARDOX500, HARDOX550, HARDOX600,HARDOX630.

    8. Bisplate:

    BISPLATE 100, BISPLATE 360, BISPLATE 400, BISPLATE 450, BISPLATE 500, BISPLATE 600

    9. NM Plate

    10. High Mn Steel Plate

    Our Photos for Wear Plate:

    Wear Plate

    Our Experience for Wear Plate:

    • 13 Year Experience in Heat-resistant Steel Field
    • 18 Year Expertise in Wear-resistant Material Field
    • 20 Year Customer-made High Quality Castings & Forgings
    Trading Terms:
    1. The nearest seaport: Shanghai port
    2. The nearest airport: Shanghai Pudong airport
    3. Payment Terms:L/C,TT,West Union,Paypal
    4. Payment Condition:50% before production, 50% before delivery against complete set of inspection report
    5. Supply Capability:  10,000 tons per year
    6. Sample Availability: yes
    7. Sample Time:15-30 Days
    8. Packing: Plywood Cases or Steel Crates
    9. Delivery time: 45 working days per 20 tons regular castings & forgings
    10. Service: OEM, ODM or Customized

    ZAlCu10 High precision Alu Cast Parts EB9090

    1. 20-year Foundry Operation Experience.
    2. Friendly & High Efficient Technical & Commercial Communication.
    3. Professional Export Practices: Exported to +60 Overseas Countries.

    [carousel_slide id=’765′]