Ni-Hard Wear Plates and Liner Plates for Chutes and Hopper Wear Protection

  • Brand: EB
  • Ni-Hard Wear Plate
  • Heat-resistant Steel Plate
  • High-temperature Alloy Plate






    Description

    ZAlCu10 High precision Alu Cast Parts EB9090

    Ni-Hard Wear Plates and Liner Plates

    • Ni-Hard Wear Plates and Liner Plates for Shot Blast Machines, Chutes, Clinker Silo,Port Machinery and Ball Mills
    • This specification covers a group of white cast irons that have been alloyed to secure high resistance to abrasive wear
    • in the applications of the mining, milling, earth-handling, and manufacturing industries. These alloys are made by melting
    • process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases,
    • minor amounts of graphite or pearlite. The following conditions for casting will be supplied: as-cast, as-cast and stress relieved,
    • hardened, hardened and stress relieved, or softened for machining. Heat treatment shall be done. The chemical composition of
    • a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel,
    • chromium, molybdenum, copper, phosphorus, and sulfur. Hardness test shall also be made.
    • Plate Thickness is10mm, 12mm, 14mm, 15mm, 16mm, 18mm, 20mm, 15mm, 30mm, 32mm, 40mm, 50mm, 60mm,
    • 80mm, 100mm, 200mm, 500mm, 1000mm.
    • Section Thickness is1 inch, 2″, 3″, 4″, 5″, 8″, 10″, 20″, 30″, 40″.
    • Material Grade is Cr-Mo Alloy Steel(ZG50Cr5Mo,ZG60Cr6Mo,Cr12Mo), high Cr white iron(BTMCr15Mo,BTMCr20Mo,BTMCr26Mo)

    Our Ni-Hard Wear Plates and Liner Plates Capability:

    We can fabricate the Ni-hard wear plates and liner plates as per your material and your sizes.

    We’d like to help select suitable material grade for your wear plates as per your specific working condition.

    Ni-Hard Wear Plates and Liner Plates Material Grades

    Standard Specification for Cr-Mo Alloy Steel
    Reference Standard Nominal Chemical Composition (W%)
    C Si Mn Cr Mo Ni P S
    AS 2017/L2A 0.45-0.55 ≤0.75 0.50-1.00 0.80-1.20 ≤0.04 ≤0.04
    AS 2017/L2B 0.55-0.65 ≤0.75 0.50-1.00 0.80-1.50 0.2-0.4 ≤0.04 ≤0.04
    AS 2017/L2C 0.70-0.90 ≤0.75 0.50-1.20 1.30-2.40 0.2-0.4 ≤0.04 ≤0.04
    ZG42Cr2Si2MnMo 0.38-0.48 1.5-1.8 0.8-1.2 1.8-2.2 0.2-0.6 ≤0.04 ≤0.04
    ZG45Cr2Mo 0.40-0.48 0.8-1.2 0.4-1.0 1.7-2.0 0.8-1.2 ≤0.5 ≤0.04 ≤0.04
    ZG30Cr5Mo 0.25-0.35 0.4-1.0 0.5-1.2 4.0-6.0 0.2-0.8 ≤0.5 ≤0.04 ≤0.04
    ZG40Cr5Mo(FED-4A) 0.35-0.45 0.4-1.0 0.5-1.2 4.0-6.0 0.2-0.8 ≤0.5 ≤0.04 ≤0.04
    ZG50Cr5Mo 0.45-0.55 0.4-1.0 0.5-1.2 4.0-6.0 0.2-0.8 ≤0.5 ≤0.04 ≤0.04
    ZG60Cr5Mo 0.55-0.65 0.4-1.0 0.5-1.2 4.0-6.0 0.2-0.8 ≤0.5 ≤0.04 ≤0.04
    FMU-29 0.25-0.45 0.3-1.0 0.6-1.5 6.0-8.0 0.2-0.4 ≤0.04 ≤0.04
    FMU-11 0.90-1.30 0.3-1.0 0.6-1.5 11.0-13.0 0.3-0.5 ≤0.04 ≤0.04
    FMU-13 0.80-1.30 0.4-1.2 0.8-1.5 11.0-13.0 0.4-0.8 ≤0.04 ≤0.04
    FMU-14 1.60-2.00 0.4-1.2 0.8-1.5 11.0-13.0 0.6-1.0 ≤0.04 ≤0.04

    2.Ni-Hard Wear Plates and Liner Plates

    Ni-hard 1: ≥ HB500 G-X 330 NiCr 4 2 0.9625

    Cast Iron Ni-hard 2: ≥ HB550 G-X 3260 NiCr 4 2 0.9620

    White Iron Ni-hard 4: ≥ HB600, HB630 G-X 300 NiCrSi 9 5 2 0.9630

    ISO 21988/JN/ HBW C Si Mn P S Ni Cr
    HBW480Cr2 480 2.5-3.0 0.8 0.8 0.10 0.10 3.0-5.5 1.5-3.0
    HBW500Cr9 500 2.4-2.8 1.5-2.2 0.2-0.8 0.06 0.06 4.0-5.5 8.0-10.0
    HBW510Cr2 510 30.-3.6 0.8 0.8 0.10 0.10 3.0-5.5 1.5-3.0
    HBW555Cr9 555 2.5-3.5 1.5-2.5 0.3-0.8 0.08 0.08 4.5-6.5 8.0-10.0
    HBW630Cr9 630 3.2-3.6 1.5-2.2 0.2-0.8 0.06 0.06 4.0-5.5 8.0-10.0

    3. Martensitic Cr- Mo Alloy Steel Hardness is ≥HRC484. Pearlitic Cr-Mo Alloy Steel Hardness is HB310-375

    4. Heat-resistant Steel Plates.

    5. High-temperature Alloy Plates.

    6. Hardox Plates include HARDOX400,HARDOX450, HARDOX500, HARDOX550, HARDOX600,HARDOX630.

    7. Bisplate includes BISPLATE 100, BISPLATE 360, BISPLATE 400, BISPLATE 450, BISPLATE 500, BISPLATE 600

    8. NM Plate

    9. High Mn Steel Plate

    Our Photos for Ni-Hard Wear Plates and Liner Plates:

     

    Ni-Hard Wear Plates and Liner Plates

    Our Experience:

    • 13 Year Experience in Heat-resistant Steel Field
    • 18 Year Expertise in Wear-resistant Material Field
    • 20 Year Customer-made High Quality Castings & Forgings

    Trading Terms:

    1. The nearest seaport: Shanghai port
    2. The nearest airport: Shanghai Pudong airport
    3. Payment Terms:L/C,TT,West Union,Paypal
    4. Payment Condition:50% before production, 50% before delivery against complete set of inspection report
    5. Supply Capability:  10,000 tons per year
    6. Sample Availability: yes
    7. Sample Time:15-30 Days
    8. Packing: Plywood Cases or Steel Crates
    9. Delivery time: 45 working days per 20 tons regular castings & forgings
    10. Service: OEM, ODM or Customized

    ZAlCu10 High precision Alu Cast Parts EB9090

    1. 20-year Foundry Operation Experience.
    2. Friendly & High Efficient Technical & Commercial Communication.
    3. Professional Export Practices: Exported to +60 Overseas Countries.

    [carousel_slide id=’765′]