Crusher Liner Plate

  • Brand: EB
  • Ni-Hard Wear Plate
  • Heat-resistant Steel Plate
  • High-temperature Alloy Plate






    描述

    Crusher Liner Plate

    Crusher Liner Plate for Shot Blast Machines, Chutes, Clinker Silo, Port Machinery and Ball Mills that have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.
    These alloys are made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite.
    The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining.
    Heat treatment shall be done.
    The chemical composition of a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum, copper, phosphorus, and sulfur. Hardness test shall also be made.
    Plate Thickness is: 10mm, 12mm, 14mm, 15mm, 16mm, 18mm, 20mm, 15mm, 30mm, 32mm, 40mm, 50mm, 60mm, 80mm, 100mm, 200mm, 500mm, 1000mm.
    Section Thickness is: 1 inch, 2″, 3″, 4″, 5″, 8″, 10″, 20″, 30″, 40″.
    Material Grade is: Cr-Mo Alloy Steel (ZG50Cr5Mo, ZG60Cr6Mo, Cr12Mo)
    High Cr white iron(BTMCr15Mo, BTMCr20Mo, BTMCr26Mo)

    Our Crusher Liner Plate Capability:

    1. We can fabricate the Ni-hard wear plates and liner plates as per your material and your sizes.
    2. We’d like to help select suitable material grade for your wear plates as per your specific working condition.
    Our Photos for Crusher Liner Plate:

    Crusher Liner Plate Crusher Liner Plate Crusher Liner Plate Crusher Liner Plate

    Cr Mo Crusher Liner Plate Material Grades
    Reference StandardNominal Chemical Composition (W%)
    CSiMnCrMoNiPS
    AS 2017/L2A0.45-0.55≤0.750.50-1.000.80-1.20≤0.04≤0.04
    AS 2017/L2B0.55-0.65≤0.750.50-1.000.80-1.500.2-0.4≤0.04≤0.04
    AS 2017/L2C0.70-0.90≤0.750.50-1.201.30-2.400.2-0.4≤0.04≤0.04
    ZG42Cr2Si2MnMo0.38-0.481.5-1.80.8-1.21.8-2.20.2-0.6≤0.04≤0.04
    ZG45Cr2Mo0.40-0.480.8-1.20.4-1.01.7-2.00.8-1.2≤0.5≤0.04≤0.04
    ZG30Cr5Mo0.25-0.350.4-1.00.5-1.24.0-6.00.2-0.8≤0.5≤0.04≤0.04
    ZG40Cr5Mo (FED-4A)0.35-0.450.4-1.00.5-1.24.0-6.00.2-0.8≤0.5≤0.04≤0.04
    ZG50Cr5Mo0.45-0.550.4-1.00.5-1.24.0-6.00.2-0.8≤0.5≤0.04≤0.04
    ZG60Cr5Mo0.55-0.650.4-1.00.5-1.24.0-6.00.2-0.8≤0.5≤0.04≤0.04
    FMU-290.25-0.450.3-1.00.6-1.56.0-8.00.2-0.4≤0.04≤0.04
    FMU-110.90-1.300.3-1.00.6-1.511.0-13.00.3-0.5≤0.04≤0.04
    FMU-130.80-1.300.4-1.20.8-1.511.0-13.00.4-0.8≤0.04≤0.04
    FMU-141.60-2.000.4-1.20.8-1.511.0-13.00.6-1.0≤0.04≤0.04

    Ni-Hard Crusher Liner Plate
    Ni-hard 1: ≥ HB500 G-X 330 NiCr 4 2 0.9625
    Cast Iron Ni-hard 2: ≥ HB550 G-X 3260 NiCr 4 2 0.9620
    White Iron Ni-hard 4: ≥ HB600, HB630 G-X 300 NiCrSi 9 5 2 0.9630

    ISO 21988/JN/HBWCSiMnPSNiCr
    HBW480Cr24802.5-3.00.80.80.100.103.0-5.51.5-3.0
    HBW500Cr95002.4-2.81.5-2.20.2-0.80.060.064.0-5.58.0-10.0
    HBW510Cr251030.-3.60.80.80.100.103.0-5.51.5-3.0
    HBW555Cr95552.5-3.51.5-2.50.3-0.80.080.084.5-6.58.0-10.0
    HBW630Cr96303.2-3.61.5-2.20.2-0.80.060.064.0-5.58.0-10.0

    Martensitic Cr- Mo Alloy Steel Hardness is ≥HRC484.
    Pearlitic Cr-Mo Alloy Steel Hardness is HB310-375

    Our Experience:
    • 13 Year Experience in Heat-resistant Steel Field
    • 18 Year Expertise in Wear-resistant Material Field
    • 20 Year Customer-made High Quality Castings & Forgings

    Trading Terms:

    1. The nearest seaport: Shanghai port
    2. The nearest airport: Shanghai Pudong airport
    3. Payment Terms:L/C,TT,West Union,Paypal
    4. Payment Condition:50% before production, 50% before delivery against complete set of inspection report
    5. Supply Capability:  10,000 tons per year
    6. Sample Availability: yes
    7. Sample Time:15-30 Days
    8. Packing: Plywood Cases or Steel Crates
    9. Delivery time: 45 working days per 20 tons regular castings & forgings
    10. Service: OEM, ODM or Customized

    ZAlCu10 High precision Alu Cast Parts EB9090

    1. 20-year Foundry Operation Experience.
    2. Friendly & High Efficient Technical & Commercial Communication.
    3. Professional Export Practices: Exported to +60 Overseas Countries.