Description
AS2074 L2B Material Wear Plates
- Material Grade: AS2074 L2B
- Production Process: Sand Process
- Hardness: HRC33~42
- Surface Finish: Appro.Ra100
- Size Tolerance: as per CT13
- Microstructure: Pearlitic + Carbonate
- Material Group: Pearlitic Cr Mo Alloy Steel AS2074 L2B, Martensitic Cr-Mo Alloy Steel.
- Heat treatment Process: quenching & tempering treatment to achieve higher hardness and ideal impact value.
- Application: Lifter Bars embedded into rubber for SAG Mills, Heavy Impact Plates
Our Photos for AS2074 L2B Wear Plates:
Wear Plates Chemistry Standard:
| Reference Standard | Nominal Chemical Composition (%) | |||||||
| C | Si | Mn | Cr | Mo | Ni | S | P | |
| AS2074/L2A | 0.45-0.55 | ≤0.75 | 0.50-1.00 | 0.80-1.20 | —— | —— | ≤0.04 | ≤0.04 |
| AS2074/L2B | 0.55-0.65 | ≤0.75 | 0.50-1.00 | 0.80-1.50 | 0.2-0.4 | —— | ≤0.04 | ≤0.04 |
| AS2074/L2C | 0.70-0.90 | ≤0.75 | 0.8-1.2 | 1.30-2.40 | 0.2-0.4 | —— | ≤0.04 | ≤0.04 |
| ZG42Cr2Si2MnMo | 0.38-0.48 | 1.5-1.8 | 0.4-1.0 | 1.8-2.2 | 0.2-0.6 | —— | ≤0.04 | ≤0.04 |
| ZG45Cr2Mo | 0.40-0.48 | 0.8-1.2 | 0.5-1.2 | 1.7-2.0 | 0.8-1.2 | ≤0.5 | ≤0.04 | ≤0.04 |
| ZG30Cr5Mo | 0.25-0.35 | 0.4-1.0 | 0.5-1.2 | 4.0-6.0 | 0.2-0.8 | ≤0.5 | ≤0.04 | ≤0.04 |
| ZG40Cr5Mo (FED-4A) | 0.35-0.45 | 0.4-1.0 | 0.5-1.2 | 4.0-6.0 | 0.2-0.8 | ≤0.5 | ≤0.04 | ≤0.04 |
| ZG50Cr5Mo | 0.45-0.55 | 0.4-1.0 | 0.5-1.2 | 4.0-6.0 | 0.2-0.8 | ≤0.5 | ≤0.04 | ≤0.04 |
| ZG60Cr5Mo | 0.55-0.65 | 0.4-1.0 | 0.6-1.5 | 4.0-6.0 | 0.2-0.8 | ≤0.5 | ≤0.04 | ≤0.04 |
| FMU-29 | 0.25-0.45 | 0.3-1.0 | 0.6-1.5 | 6.0-8.0 | 0.2-0.4 | —— | ≤0.04 | ≤0.04 |
| FMU-11 | 0.90-1.30 | 0.3-1.0 | 0.6-1.5 | 11.0-13.0 | 0.3-0.5 | —— | ≤0.04 | ≤0.04 |
| FMU-13 | 0.80-1.30 | 0.4-1.2 | 0.8-1.5 | 11.0-13.0 | 0.4-0.8 | —— | ≤0.04 | ≤0.04 |
| FMU-14 | 1.60-2.00 | 0.4-1.2 | 0.8-1.5 | 11.0-13.0 | 0.6-1.0 | —— | ≤0.04 | ≤0.04 |
Our Experience:
- 13 Year Experience in Heat-resistant Steel Field
- 18 Year Expertise in Wear-resistant Material Field
- 20 Year Customer-made High Quality Castings & Forgings
Trading Terms:
- The nearest seaport: Shanghai port
- The nearest airport: Shanghai Pudong airport
- Payment Terms:L/C,TT,West Union,Paypal
- Payment Condition:50% before production, 50% before delivery against complete set of inspection report
- Supply Capability: 10,000 tons per year
- Sample Availability: yes
- Sample Time:15-30 Days
- Packing: Plywood Cases or Steel Crates
- Delivery time: 45 working days per 20 tons regular castings & forgings
- Service: OEM, ODM or Customized
1. 20-year Foundry Operation Experience.
2. Friendly & High Efficient Technical & Commercial Communication.
3. Professional Export Practices: Exported to +60 Overseas Countries.