Description
ASTM A297 Cobalt Alloy Castings
Heat Resistant Parts Specimens for joining were cut from the as-cast ingot.
Transient liquid phase (TLP) bonding was carried out at the standard solution cycle, using MBF-30 interlayer. Also,
bonded specimens were homogenized at the standard aging condition
Table 1 : Standard
| Cobalt Alloy Castings | Co | Cr | C | W | Mo | Ni | Si | B | Fe | Mn | Others |
| STELLITE 1 | BAL | 33 | 2.45 | 13 | – | 2.5* | 1 | – | 2.5* | 1 | – |
| STELLITE 3 | BAL | 31 | 2.5 | 13 | – | 2.5* | 1 | – | 2.5* | 1 | – |
| STELLITE 4 | BAL | 31.5 | 1 | 14 | – | 2.0* | 1 | – | 2.0* | 1 | – |
| STELLITE 6 | BAL | 28 | 1.2 | 5 | – | 3.0* | 1 | – | 2.5* | 1 | – |
| STELLITE 12 | BAL | 29 | 1.85 | 9 | – | 2.5* | 1 | – | 2.5* | 1 | – |
| STELLITE 20 | BAL | 33 | 2.45 | 17.5 | – | 2.5* | 1 | – | 2.5* | 1 | – |
| STELLITE 21 | BAL | 27 | 0.25 | – | 5.5 | 2.5* | 1 | – | 3.0* | 1 | – |
| STELLITE 31 | BAL | 26 | 0.5 | 7.5 | – | 10.5 | 1 | – | 2.0* | 1 | – |
| STELLITE 190 | BAL | 26 | 3.3 | 14 | – | 1 | 1 | – | 8 | 0.5 | – |
| STELLITE 238 | BAL | 26 | 0.1 | – | 3 | – | 1 | – | 20 | 1 | – |
| STELLITE 306 | BAL | 25 | 0.4 | 2 | – | 6 | 1 | – | 4.0* | 1 | Nb=5 |
| STELLITE 694 | BAL | 28 | 1 | 19 | – | 5 | 1 | – | 2.5* | 1 | V=1 |
| STELLITE F | BAL | 25.5 | 1.75 | 12.25 | – | 22.5 | 1 | – | 1.5* | – | – |
| STELLITE SF1 | BAL | 19 | 1.3 | 13 | – | 13 | 3 | 2.5 | 3* | 0.5 | Cu=0.5 |
| STELLITE SF6 | BAL | 19 | 0.7 | 7 | – | 13 | 2.5 | 1.7 | 3* | 0.5 | Cu=0.5 |
| STELLITE SF12 | BAL | 19 | 1 | 9 | – | 13 | 3 | 2 | 3* | 0.5 | Cu=0.5 |
| STELLITE SF20 | BAL | 19 | 1.5 | 15 | – | 13 | 3 | 3 | 2* | 0.5 | Cu=0.5 |
| TRIBALOY T400 | BAL | 8 | 0.1* | – | 28 | 3* | 2.4 | – | 3* | – | – |
| TRIBALOY T800 | BAL | 17 | 0.1* | – | 28 | 3* | 3.2 | – | 3* | – | – |
| DELORO 15 | – | – | 0.06* | – | – | BAL | 2 | 1.05 | 1.5* | 20 | Cu=20 |
| DELORO 22 | – | 0.7 | 0.1 | – | – | BAL | 2.3 | 1.75 | – | – | – |
| DELORO 40 | – | 7 | 0.1 | – | – | BAL | 3.5 | 2.25 | – | – | – |
| DELORO 50 | – | 10.25 | 0.45 | – | – | BAL | 4 | 1.85 | 4 | – | – |
| DELORO 60 | – | 14.25 | 0.6 | – | – | BAL | 2 | 3.5 | 4 | – | – |
| DELORO 625 | – | 22 | 0.1 | – | 9 | BAL | – | – | 5 | – | – |
| NISTELLE C | – | 16.5 | 0.12* | 4.5 | 17 | BAL | 0.7 | – | 6 | – | – |
| TRIBALOY T700 | – | 15 | 0.10* | – | 32 | BAL | 3.25 | – |
Table 2 : Standard
| Hastelloy C22®(UNS N06022)(Max.) | |||||||||||
| C | MN | P | S | Si | Cr | Ni | Mo | CO | Fe | W | V |
| 0.015 | 0.5 | 0.02 | 0.02 | 0.08 | 20.0-22.5 | Bal. | 12.5-14.5 | 2.5 | 2.0-6.0 | 2.5-3.5 | 0.35 |
| Hastelloy C276®(UNS N10276)(Max.) | |||||||||||
| C | MN | P | S | Si | Cr | Ni | Mo | CO | Fe | W | V |
| 0.01 | 1 | 0.04 | 0.03 | 0.08 | 14.5-16.5 | Bal. | 15.0-17.0 | 2.5 | 4.0-7.0 | 3.0-4.5 | 0.35 |
| Hastelloyx®(UNS N06002)(Max.) | |||||||||||
| C | MN | P | S | Si | Cr | Ni | Mo | CO | Fe | W | other |
| 0.05-0.15 | 1 | 0.04 | 0.03 | 1 | 20.5-23.0 | Bal. | 8.0-10.0 | 0.5-2.5 | 17.0-20.0 | 0.2-1.0 | / |
| Monel 400®(UNS NO4400) (Max.) | |||||||||||
| C | MN | S | Si | Ni | Cu | Fe | |||||
| 0.3 | 2 | 0.024 | 0.5 | 63 min | 28-34 | 2.5 | |||||
| Monel M400®(UNS NO4400)(Max.) | |||||||||||
| C | MN | S | Si | Ni | Cu | Fe | |||||
| 0.3 | 2 | 0.024 | 0.5 | 63-70 | 28-34 | 2.5 | |||||
| Monel R405®(UNS NO4405)(Max.) | |||||||||||
| C | MN | S | Si | Ni | Cu | Fe | |||||
| 0.3 | 2 | 0.025-0.06 | 0.5 | 63.0min | 28-34 | 2.5 | |||||
| Monel K500®(UNS NO5500)(Max.) | |||||||||||
| C | MN | S | Si | Ni | Cu | Ti | AI | Fe | |||
| 0.1 | 2 | 0.01 | 0.5 | 63min | 27-33 | 0.86 | 2.3-3.15 | 2 | |||
Our Photos for ASTM A297 HP Cobalt Alloy Castings:
Our Experience
- 13 Year Experience in Heat-resistant Steel Field
- 18 Year Expertise in Wear-resistant Material Field
- 20 Year Customer-made High Quality Castings & Forgings
Trading Terms:
- The nearest seaport is Shanghai port
- The nearest airport is Shanghai Pudong airport
- Payment Terms is L/C,TT,West Union,Paypal
- Payment Condition is 50% before production, 50% before delivery against complete set of inspection report
- Supply Capability is 10,000 tons per year
- Sample Availability is yes
- Sample Time is 15-30 Days
- Packing is Plywood Cases or Steel Crates
- Delivery time is 45 working days per 20 tons regular castings & forgings
- Service is OEM, ODM or Customized
1. 20-year Foundry Operation Experience.
2. Friendly & High Efficient Technical & Commercial Communication.
3. Professional Export Practices: Exported to +60 Overseas Countries.
[carousel_slide id=’765′]