Chrome Moly Steel Mill Liners
That have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling and manufacturing industries.
These alloys are made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite.
Material Grade is:
Cr-Mo Alloy Steel (ZG50Cr5Mo, ZG60Cr6Mo, Cr12Mo)
High Cr White Iron (BTMCr15Mo, BTMCr20Mo, BTMCr26Mo)
Section Thickness is: 1 inch, 2″, 3″, 4″, 5″, 8″, 10″, 20″, 30″, 40″.
Plate Thickness is: 10mm, 12mm, 14mm, 15mm, 16mm, 18mm, 20mm, 25mm, 30mm, 32mm, 40mm, 50mm, 60mm, 80mm, 100mm, 200mm, 500mm, 1000mm.
We can fabricate the Chrome Moly Steel Mill Liners as per your material and your sizes.
We’d like to help select suitable material grade for your wear plates as per your specific working condition.
Our Photos for Chrome Moly Steel Mill Liners:
Material Grades:
| Reference Standard | Nominal Chemical Composition (W%) | |||||||
| C | Si | Mn | Cr | Mo | Ni | P | S | |
| AS 2017/L2A | 0.45-0.55 | ≤0.75 | 0.50-1.00 | 0.80-1.20 | – | – | ≤0.04 | ≤0.04 |
| AS 2017/L2B | 0.55-0.65 | ≤0.75 | 0.50-1.00 | 0.80-1.50 | 0.2-0.4 | – | ≤0.04 | ≤0.04 |
| AS 2017/L2C | 0.70-0.90 | ≤0.75 | 0.50-1.20 | 1.30-2.40 | 0.2-0.4 | – | ≤0.04 | ≤0.04 |
| ZG42Cr2Si2MnMo | 0.38-0.48 | 1.5-1.8 | 0.8-1.2 | 1.8-2.2 | 0.2-0.6 | – | ≤0.04 | ≤0.04 |
| ZG45Cr2Mo | 0.40-0.48 | 0.8-1.2 | 0.4-1.0 | 1.7-2.0 | 0.8-1.2 | ≤0.5 | ≤0.04 | ≤0.04 |
| ZG30Cr5Mo | 0.25-0.35 | 0.4-1.0 | 0.5-1.2 | 4.0-6.0 | 0.2-0.8 | ≤0.5 | ≤0.04 | ≤0.04 |
| ZG40Cr5Mo (FED-4A) | 0.35-0.45 | 0.4-1.0 | 0.5-1.2 | 4.0-6.0 | 0.2-0.8 | ≤0.5 | ≤0.04 | ≤0.04 |
| ZG50Cr5Mo | 0.45-0.55 | 0.4-1.0 | 0.5-1.2 | 4.0-6.0 | 0.2-0.8 | ≤0.5 | ≤0.04 | ≤0.04 |
| ZG60Cr5Mo | 0.55-0.65 | 0.4-1.0 | 0.5-1.2 | 4.0-6.0 | 0.2-0.8 | ≤0.5 | ≤0.04 | ≤0.04 |
| FMU-29 | 0.25-0.45 | 0.3-1.0 | 0.6-1.5 | 6.0-8.0 | 0.2-0.4 | – | ≤0.04 | ≤0.04 |
| FMU-11 | 0.90-1.30 | 0.3-1.0 | 0.6-1.5 | 11.0-13.0 | 0.3-0.5 | – | ≤0.04 | ≤0.04 |
| FMU-13 | 0.80-1.30 | 0.4-1.2 | 0.8-1.5 | 11.0-13.0 | 0.4-0.8 | – | ≤0.04 | ≤0.04 |
| FMU-14 | 1.60-2.00 | 0.4-1.2 | 0.8-1.5 | 11.0-13.0 | 0.6-1.0 | – | ≤0.04 | ≤0.04 |
- Ni-Hard Wear Plates and Liner Plates
- Ni-hard 1: ≥ HB500 G-X 330 NiCr 4 2 0.9625
- Cast Iron Ni-hard 2: ≥ HB550 G-X 3260 NiCr 4 2 0.9620
- White Iron Ni-hard 4: ≥ HB600, HB630 G-X 300 NiCrSi 9 5 2 0.9630
| ISO 21988/JN/ | HBW | C | Si | Mn | P | S | Ni | Cr |
| HBW480Cr2 | 480 | 2.5-3.0 | 0.8 | 0.8 | 0.10 | 0.10 | 3.0-5.5 | 1.5-3.0 |
| HBW500Cr9 | 500 | 2.4-2.8 | 1.5-2.2 | 0.2-0.8 | 0.06 | 0.06 | 4.0-5.5 | 8.0-10.0 |
| HBW510Cr2 | 510 | 30.-3.6 | 0.8 | 0.8 | 0.10 | 0.10 | 3.0-5.5 | 1.5-3.0 |
| HBW555Cr9 | 555 | 2.5-3.5 | 1.5-2.5 | 0.3-0.8 | 0.08 | 0.08 | 4.5-6.5 | 8.0-10.0 |
| HBW630Cr9 | 630 | 3.2-3.6 | 1.5-2.2 | 0.2-0.8 | 0.06 | 0.06 | 4.0-5.5 | 8.0-10.0 |
1.Martensitic Cr- Mo Alloy Steel Hardness is ≥HRC484. Pearlitic Cr-Mo Alloy Steel Hardness is HB310-375
2. Heat-resistant Steel Plates.
3. High-temperature Alloy Plates.
Our Experience:
- 13 Year Experience in Heat-resistant Steel Field
- 18 Year Expertise in Wear-resistant Material Field
- 20 Year Customer-made High Quality Castings & Forgings
Trading Terms:
- The nearest seaport: Shanghai port
- The nearest airport: Shanghai Pudong airport
- Payment Terms:L/C,TT,West Union,Paypal
- Payment Condition:50% before production, 50% before delivery against complete set of inspection report
- Supply Capability: 10,000 tons per year
- Sample Availability: yes
- Sample Time:15-30 Days
- Packing: Plywood Cases or Steel Crates
- Delivery time: 45 working days per 20 tons regular castings & forgings
- Service: OEM, ODM or Customized
1. 20-year Foundry Operation Experience.
2. Friendly & High Efficient Technical & Commercial Communication.
3. Professional Export Practices: Exported to +60 Overseas Countries.