Description
Cement Mill Liners
Cement Mill Liners for Shot Blast Machines, Chutes, Clinker Silo,Port Machinery and Ball Mills.
Shape: Flat Plate, Arc Plate, Waved Plates, Corrugated Plates.
Bolted Plates: one-hole, two-holes, three holes, four holes, oval – hole.
Quality Level: As per National Standard & International Standards.
Production Process: Sand Process with proper heat-treatment(quenching and tempering) process to achieve ideal hardness and impact value.
The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining.
These alloys are made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite.
Photos for Cement Mill Liners :
Cement Mill Liners Application :
- Armed plates for clincker silo in cement plants.
- Wear plates for chutes, material bunkers for port machinery.
- Material hoppers in steel mills.
- High abrasion plates for material bin for port maachinery.
- Wear plates for coal hoppers.
Cement Mill Liners Special Features :
- We make Cr-Mo Alloy steel and high Cr white iron castings with Sodium Silicate Sand Process and Resin Sand Process.
- Our supply finished alloy steel castings with heat-treatment and machining process.
- We can produce Alloy Cr-Mo Steel and White Iron castings as per GB/T26651, GB/T 8263-1999, AS2074, AS2027, DIN 1695,
AISI, ASTM, JIS G 5153, NF A32401, BS4844. - Our can recommend suitable material grades of wear parts for you as per your specific working condition.
- Design of wear plates & Chute Liners.
- Width and length of wear plates determines hole pattern, regardless of thickness.
Cement Mill Liners Material Selection :
- Martensitic Cr Mo Alloy Steel (ZG50Cr5Mo, ZG60Cr6Mo, Cr12Mo): Hardness: ≥HRC48, Impact value: ≥25J.
- High Cr white iron (BTMCr15Mo, BTMCr20Mo, BTMCr26Mo): Hardness: ≥HRC56, Impact value: ≥5J.
- Ni-hard White Iron: AS2027 NiCr2-500, AS2027 NiCr1-550, AS2027 NiCr4-500, AS2027 NiCr4-600, AS2027 NiCr4-630 AS2027 NiCr2-500, AS2027 NiCr1-550, AS2027 NiCr4-500, AS2027 NiCr4-600, AS2027 NiCr4-630.
High Cr white iron:
| ISO 21988/JN/ | HBW | C | Si | Mn | P | s | Cr | Ni | Mo | Cu |
| HBW555XCr13 | 555 | 1.8-3.6 | 1 | 0.5-1.5 | 0.08 | 0.08 | 11-14 | 2 | 3 | 1.2 |
| HBW555XCr16 | 555 | 1.8-3.6 | 1 | 0.5-1.5 | 0.08 | 0.08 | 14-18 | 2 | 3 | 1.2 |
| HBW555XCr21 | 555 | 1.8-3.6 | 1 | 0.5-1.5 | 0.08 | 0.08 | 18-23 | 2 | 3 | 1.2 |
| HBW555XCr27 | 555 | 1.8-3.6 | 1 | 0.5-1.5 | 0.08 | 0.08 | 23-30 | 2 | 3 | 1.2 |
| HBW600XCr35 | 600 | 3.0-5.5 | 1 | 1.0-3.0 | 0.06 | 0.06 | 30-40 | 1 | 1.5 | 1.2 |
| HBW600XCr20Mo2Cu | 600 | 3.0-5.5 | 1 | 1 | 0.06 | 0.06 | 18-21 | 1 | 1.4-2.0 | 0.8-1.2 |
| ISO 21988/JN/ | HBW | C | Si | Mn | P | S | Ni | Cr |
| HBW480Cr2 | 480 | 2.5-3.0 | 0.8 | 0.8 | 0.1 | 0.1 | 3.0-5.5 | 1.5-3.0 |
| HBW500Cr9 | 500 | 2.4-2.8 | 1.5-2.2 | 0.2-0.8 | 0.06 | 0.06 | 4.0-5.5 | 8.0-10.0 |
| HBW510Cr2 | 510 | 30.-3.6 | 0.8 | 0.8 | 0.1 | 0.1 | 3.0-5.5 | 1.5-3.0 |
| HBW555Cr9 | 555 | 2.5-3.5 | 1.5-2.5 | 0.3-0.8 | 0.08 | 0.08 | 4.5-6.5 | 8.0-10.0 |
| HBW630Cr9 | 630 | 3.2-3.6 | 1.5-2.2 | 0.2-0.8 | 0.06 | 0.06 | 4.0-5.5 | 8.0-10.0 |
Experience:
- 13 Year Experience in Heat-resistant Steel Field
- 18 Year Expertise in Wear-resistant Material Field
- 20 Year Customer-made High Quality Castings & Forgings
Trading Terms:
- The nearest airport: Shanghai Pudong airport
- Payment Terms:L/C,TT,West Union,Paypal
- Payment Condition:50% before production, 50% before delivery against complete set of inspection report
- Supply Capability: 10,000 tons per year
- Sample Availability: yes
- Sample Time:15-30 Days
- Packing: Plywood Cases or Steel Crates
- Delivery time: 45 working days per 20 tons regular castings & forgings
- Service: OEM, ODM or Customized
- 20-year Foundry Operation Experience.
- Friendly & High Efficient Technical & Commercial Communication
- Professional Export Practices: Exported to +60 Overseas Countries.