Cement Mill Liner

Description

Cement Mill Liner

Cement Mill Liner for Shot Blast Machines, Chutes, Clinker Silo,Port Machinery and Ball Mills.
This specification covers a group of white cast irons that have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.
These alloys are made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite.
The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining.
Heat treatment shall be done.
The chemical composition of a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum, copper, phosphorus, and sulfur. Hardness test shall also be made.

1. Shape: Flat Plate, Arc Plate, Waved Plates, Corrugated Plates.
2. Bolted Plates: one-hole, two-holes, three holes, four holes, oval – hole.
3. Quality Level: As per National Standard & International Standards.
4. Production Process: Sand Process with proper heat-treatment(quenching and tempering) process to achieve ideal hardness and impact value.

Photos for Cement Mill Liner :

Cement Mill Liner Application :

• Armed plates for clincker silo in cement plants.
• Wear plates for chutes, material bunkers for port machinery.
• Material hoppers in steel mills.
• High abrasion plates for material bin for port maachinery.
• Wear plates for coal hoppers.

Cement Mill Liner Special Features :

1. We make Cr-Mo Alloy steel and high Cr white iron castings with Sodium Silicate Sand Process and Resin Sand Process.
2. Our supply finished alloy steel castings with heat-treatment and machining process.
3. We can produce Alloy Cr-Mo Steel and White Iron castings as per GB/T26651, GB/T 8263-1999, AS2074, AS2027, DIN 1695,
   AISI, ASTM, JIS G 5153, NF A32401, BS4844.
4. Our can recommend suitable material grades of wear parts for you as per your specific working condition.
5. Design of wear plates & Chute Liners. Width and length of wear plates determines hole pattern, regardless of thickness.
6. Material Selection of Wear Plates & Chute Liners.

Cement Mill Liner Material Grade :

1. Martensitic Cr Mo AlloySteel (ZG50Cr5Mo, ZG60Cr6Mo, Cr12Mo): Hardness: ≥HRC48, Impact value: ≥25J.
2. High Cr white iron (BTMCr15Mo, BTMCr20Mo, BTMCr26Mo): Hardness: ≥HRC56, Impact value: ≥5J.
3. Ni-hard White Iron: AS2027 NiCr2-500, AS2027 NiCr1-550, AS2027 NiCr4-500, AS2027 NiCr4-600, AS2027 NiCr4-630 AS2027 NiCr2-500, AS2027 NiCr1-550, AS2027 NiCr4-500, AS2027 NiCr4-600, AS2027 NiCr4-630.

1. High Cr white iron:

2. Ni hard white Iron:

• Handelsname Kurzzeichen W.St.Nr.
• Ni-hard 1: ≥ HB500 G-X 330 NiCr 4 2 0.9625
• Ni-hard 2: ≥ HB550 G-X 3260 NiCr 4 2 0.9620
• Ni-hard 4: ≥ HB600, HB630 G-X 300 NiCrSi 9 5 2 0.9630
• G-X 300 NiMo 15 3 0.9635
• G-X 260 Cr 27 0.9635

3. Martensitic Cr- Mo Alloy Steel: Hardness: ≥HRC48
4. Pearlitic Cr-Mo Alloy Steel Hardness: HB310-375
5. Heat-resistant Steel Plates.
6. High-temperature Alloy Plates.

Hardox Plates: HARDOX400, HARDOX450, HARDOX500, HARDOX550, HARDOX600, HARDOX630.
Bisplate:
BISPLATE 100, BISPLATE 360, BISPLATE 400, BISPLATE 450, BISPLATE 500, BISPLATE 600

Plate Thickness:
10mm, 12mm, 14mm, 15mm, 16mm, 18mm, 20mm, 15mm, 30mm, 32mm, 40mm, 50mm, 60mm, 80mm, 100mm, 200mm, 500mm, 1000mm.
Section Thickness: 1inch, 2″, 3″, 4″, 5″, 8″, 10″, 20″, 30″, 40″.

Experience:

• 13 Year Experience in Heat-resistant Steel Field
• 18 Year Expertise in Wear-resistant Material Field
• 20 Year Customer-made High Quality Castings & Forgings

Trading Terms:

1. The nearest seaport: Shanghai port
2. The nearest airport: Shanghai Pudong airport
3. Payment Terms:L/C,TT,West Union,Paypal
4. Payment Condition:50% before production, 50% before delivery against complete set of inspection report
5. Supply Capability:  10,000 tons per year
6. Sample Availability: yes
7. Sample Time:15-30 Days
8. Packing: Plywood Cases or Steel Crates
9. Delivery time: 45 working days per 20 tons regular castings & forgings
10. Service: OEM, ODM or Customized

1.  20-year Foundry Operation Experience.
2. Friendly & High Efficient Technical & Commercial Communication
3. Professional Export Practices: Exported to +60 Overseas Countries.

High Cr Wear Plates

High Temperature Heat-treatment Fixture

Nickel Alloy Castings & Forgings