Advantages and Characteristics of Heat Treatment Material Basket

Heat treatment material Basket frame does not need to be expanded and contracted. The stainless steel plates are gradually selected, and the result is very easy to be invalid, the service life is very short, and the cost is very high. Afterwards, according to the exploration, the very general A3 steel was selected, and unexpected practical results were obtained, with long life, little deformation, and low cost.

The heat treatment material Basket frame does not need to expand and contract. If stainless steel plates are used, the result is very easy to be invalid, the service life is very short, and the cost is high. It is recommended to use very general A3 steel, which has very good effect, long life, little deformation and low cost.

Heat treatment method:

Heat Treatment Material Basket Heat Treatment Material Basket

Quenching operation method:

After heating the steel to Ac3+30~50°C or Ac1+30~50°C or below Ac1 temperature (you can check the related materials), it is generally cooled slowly according to the temperature control.

Quenching operation method:

heat the steel to 30~50 degrees above Ac3 or Accm, and cool it at a cooling rate slightly higher than quenching after heat insulation.

Quenching operation method:

heat the steel parts above the changing temperature Ac3 or Ac1, heat insulation for a period of time, and then quickly cool in water, nitrate, oil, or air. Purpose: Quenching is generally to better obtain high-toughness austenitic structure, sometimes when quenching some ferritic stainless steels (such as stainless steel plates, wear-resistant steel plates), it is to better obtain a single uniform Martensite Body structure to improve wear resistance and corrosion resistance.

Heat Treatment Material Basket

Quenching operation method:

heat the quenched steel parts to a temperature below Ac1 again, and cool in gas or oil, boiling water, and water after heat insulation.

Heat treatment operation method:

high temperature quenching after quenching is called heat treatment. The steel parts are heated to a temperature 10-20 degrees higher than that during quenching. After heat preservation, quenching is carried out, and then quenching is carried out at a temperature of 400-720 degrees.

Time-sensitive operation method:

heat the steel parts to 80~200 degrees, heat insulation for 5~20 hours or longer, and then take it out of the furnace and cool it in the air. Purpose: 1. Stabilize the structure of the steel after quenching, reduce the deformation during storage or application; 2. Relieve the thermal stress after quenching and cutting production, and stabilize the appearance and specifications.

Cold force operation method:

Cool the quenched steel parts in ultra-low temperature materials (such as liquid nitrogen, liquid nitrogen) to -60 to -80 degrees or lower, and then remove the uniform temperature to the room temperature after the temperature is uniform.

Heat Treatment Material Basket Heat Treatment Material Basket

Flame heating surface quenching operation method:

use a flame burning with oxygen-acetylene gas mixture to spray on the surface of the steel, and quickly heat it. When the quenching temperature is reached, immediately spray water to cool.

Electromagnetic induction heating surface quenching operation method:

put the steel part into the sensor, cause the surface of the steel part to induce an electromotive force, heat it to the quenching temperature in a very short time, and then sprinkle water to cool it.

Nitriding operation method:

Put the steel part into the nitriding material, heat it to 900-950 degrees and heat insulation, so that the surface of the steel part can obtain a certain concentration value and deep nitriding layer.

Nitriding operation method:

using specific nitrogen atoms dissolved out of nitrogen dioxide at 500-600 degrees to make the surface of the steel part saturated with nitrogen to produce a nitriding layer.

Niurizing operation method:

Additional nitriding and high-frequency quenching to the surface of the steel part. Purpose: To improve the strength, wear resistance, fatigue limit and anti-corrosion ability of the surface layer of steel parts

Heat Treatment Material Basket Heat Treatment Material Basket

Q&A:

Q: Do you provide free samples?
A: Yes, usually we provide free samples for testing under the condition of freight paid by customer.

Q: What is the Warranty for our products ?
A: If any quality problems on our side occurred in this period , we will take on the shipping cost and replacement.

Q: Can you manufacture Customization products?
A: Yes, we can.
We can produce both standard and special prosucts.
Our can make them according to your drawings and samples.

Q: What information do we need to provide to you in order to confirm our parts order?
A: provide us your drawings or detailed specifications for our technical staff could make the drawing.

Q: What is the delivery time of your products?
A: It depends on the inventory availability.If items needed are in stock, the delivery time would be within 7 work days, but if not the delivery time would be around 30 work days.

We will send working schedule of your order each week.
Our will inspect and test all merchandise in case of damaging and missing parts before shipment.
The detailed inspection picturesion by email.

 

Eternal Bliss Alloy Casting & Forging Co, Ltd.

Caesar

E-mail: sales@ebcastworld.com

What’s app: 0086-130 930 23772

www.ebcastworld.com